Ugin e.ON sinter fast, Instructions For Use Manual

Instructions for use (rev 011221) 

e.ON sinter fast + 

UGIN DENTAIRE 

21

7.

ADVICES - PRECAUTIONS FOR USE 

GENERAL

-

During operation and after use, the surface of 

the furnace head may become very hot: avoid 
direct contact

 with the skin 

(risk of burns).

-

eON sinter fast + is equipped with 

heat 

extractors

 to control the temperature of the 

components and guarantee safety: 

do not 

cover the furnace during use 

and 

do not place 

objects

 around the furnace or in front of the 

ventilation openings. 

CYCLE START AND CONFIGURATION

-

Do not open the platform during high 
temperature cycles

: danger of burns and risk of 

irreversible damage to heating elements and 
refractories. 

-

At the end of the cycle, 

the temperature must 

be lower than 300°C before opening the 
furnace. Do not switch off the power supply

, 

because heat extractors are stopped and the 
internal temperature increases and can 
damage the equipment. 

-

If the 

temperature is above 300°C, it is not 

possible to start a cycle

 (risk of damaging the 

refractories.) Wait for cooling: temperature 
displayed on the screen below 300°C. 

-

When the 

temperature is below 200°C, the 

power supply can be switched off

 (switch at 

the back of furnace). 

-

At the end of the cycle, the furnace 
automatically returns to the 

standby position

.  

-

When the 

furnace is in standby or off, the 

platform must be in the high position

 to avoid 

condensation. 

-

Do not touch the display during a cycle

 to 

avoid manual interruption of the programme. 

-

At the start of the cycle, avoid using an 
increase rate too fast

 to avoid damaging the 

heating elements. Likewise, 

a large difference 

between two increase rates is not 
recommended.

-

Observe the recommendations of the 
manufacturer of Zirconia

 to avoid significant 

gaseous emissions which may damage the 
muffle.

-

For the first time or after a long time without 
use, need to 

preheat 

to eliminate condensation 

and avoid fractures of the refractory material: 

launch a decontamination program (No. 40).

-

Zirconia sintering temperatures are given as 
indicative by disc manufacturer. 

If necessary, 

these one can be adjusted from -15°C and up 
to +50°C around the final temperature 
recommended. 

-

Comply with the recommendations of the 
manufacturer of the zirconia used to verify 
compatibility with the perform of a short 
program and the maximum number of 
elements in short cycle

. Follow its instructions 

for programming within the technical limits of 
the e.ON sinter fast + (

the value of the heating 

rate must be less than 94°C /min up to 1000°C).

HEATING ELEMENTS (RODS) 

-

Molybdenum silicon rods are very brittle at 
room temperature: 

do not handle them.

-

The 

heating

elements must not be maintained 

for long periods between 400°C and 700°C

 to 

avoid their oxidation.